EN10216-2 15NiCuMoNb5-6-4 (WB36) High Pressure Boiler Tube
- EN10216-2
- China
- Stock
- 15NiCuMoNb5-6-4,DIWA 373, WB36
15NiCuMoNb5-6-4 (DIWA 373, WB36) is alloyed with several alloying elements such as Ni-Cu-Mo-Nb, which not only greatly improves the high temperature strength and temperature of the steel, but also has good comprehensive mechanical propertie
EN10216-2 15NiCuMoNb5-6-4 (WB36) High Pressure Boiler Tube
EN10216-2 15NiCuMoNb5-6-4 (DIWA 373, WB36) High Pressure Boiler Tube
15NiCuMoNb5-6-4 steel grade is one of grade in EN 10216-2, it is widely used in large diameter seamless high pressure boiler tubes
15NiCuMoNb5-6-4 (DIWA 373, 15NiCuMoNb5, or WB36) is a high-temperature, high-strength, high-strength, high-strength structural steel developed by Germany in the 1930s. The steel is alloyed with several alloying elements such as Ni-Cu-Mo-Nb, which not only greatly improves the high temperature strength and temperature of the steel, but also has good comprehensive mechanical properties and hot workability. And solderability.
Manufacture
15NiCuMoNb5-6-4 (WB36) high pressure boiler tubes are manufactured by seamless process.
EN10216-2 15NiCuMoNb5-6-4 (WB36) High Pressure Boiler Tubes Quick Details
Type:Seamless Steel tubes
Technique: Hot rolled or cold drawn
Standard: EN 10216-2
Outside Diameter: 25mm-508mm
Wall thickness: 6mm-35mm
Length: 6000Mm, 12000m or specified length as required.
Type of End-Finish: Plain End, Beveled End, Treaded
Surface treatment: Tubes will be varnished (Outside only) to prevent rust.
Additional Info
Payment Terms:T/ T, LC
Port of Shipment: Tianjin, China
Package:According To Per Customers' Require
Marking: Standard + Steel Grade + Size + Heat No + Lot No
Delivery time: Tubes will be completed within 30 days, and urgent delivery time can be discussed.
Chemical composition of 15NiCuMoNb5-6-4
| Standard | Grade | C | Mn | Si | P | S | Cr | Cu | Mo | Ni | Nb | N |
| EN 10216-2 | 15NiCuMoNb5-6-4 | 0.10-0.17 | 0.8-1.2 | 0.25-0.50 | ≤0.03 | ≤0.025 | ≤0.30 | 0.5-0.8 | 0.25-0.50 | 1.00-1.30 | 0.015-0.045 | ≤0.02 |
Microstructure
The supply condition of 15NiCuMoNb5-6-4 (DIWA 373, WB36) steel pipe is normalizing (quenching) + tempering. After the final heat treatment of normalizing + tempering,
The metallographic structure is bainite + ferrite + sorbite or bainite + a small amount of ferrite.
Mechanical properties of 15NiCuMoNb5-6-4
| Grade | Yield Strength/MPa | Tensile Strength/Mpa | Elongation/% | Hardness/HB | Impact work longitudinal/J | Microstructure | ||
| 20℃ | 0℃ | -20℃ | ||||||
| 15NiCuMoNb5-6-4 | ≥440 | 610-680 | ≥19 | ≤252 | ≥95 | ≥80 | ≥60 | F+B+P |
Durable strength σ, 15NiCuMoNb5-6-4 (WB36) high pressure boiler tube
| Grade | 400℃ | 420℃ | 440℃ | 460℃ | 480℃ | 490℃ | 500℃ |
| 15NiCuMoNb5-6-4 | 373 | 325 | 273 | 210 | 139 | 104 | 69 |
Heat treatment
| Normalizing or quenching | Temper | Stress relief heat treatment |
| 900-980 ° C air cooling | 580-640 ° C air cooling | 550-600 ° C air cooling |
| 880-930 ° C oil or water cooling | 620-700 ° C air cooling |
The temperature for the stress relief treatment should be 30 ° C lower than the actual tempering temperature.
The heating of the steel pipe should be carried out completely and thoroughly. When the steel tube is heated to the quenching temperature, the holding time is 1 minute per mm / (wall thickness is less than 20 mm, at least 20 minutes). The tempering and stress-relieving holding time is calculated according to the wall thickness of 2 minutes per mm, and the minimum is not less than 30 minutes.
Welded
EN10216-2 15NiCuMoNb5-6-4 steel pipe has good welding performance. Manual welding electrode L-80 (AWS-E11016G), tungsten argon arc welding wire with SMH-80 (AWS-E110S) or the corresponding domestic welding materials. In order to avoid welding cracks, preheating is required before welding (temperature is 150-200 ° C). De-stressing treatment after welding.
WB36 has good solderability. The cold crack is more sensitive, but preheating at 150 °C can prevent cold cracks and is not sensitive to reheat cracks. Manual arc welding with electrode CHE607NI base H10Mn2NiMoA/H08Mn2MoA welding wire with SJ101 flux submerged arc automatic welding, after 530-600 °C post-weld heat treatment has good performance, can meet the manufacturing requirements.
Application
EN10216-2 15NiCuMoNb5-6-4 (DIWA 373, WB36) steel pipe has good comprehensive performance and can be widely used in steam drums, steam-water separators in supercritical units, water-cooled wall headers and steam generators with working temperature of 400 °C. Pressure pipes with a wall temperature of 500 ° C, and high temperature and high pressure components such as nuclear power equipment.
Since the strength grade of DIWA 373 (WB36) is higher than 20G and SA106C, the use of this steel will significantly reduce the wall thickness of the steel pipe and greatly reduce the amount of materials, which has good economic benefits.