ASTM A334 Grade 3 Low-Temperature Seamless and Welded Tubes
- ASTM A334/ASME SA334
- China
- Stock,Production
- Grade 3
ASTM A334 Grade 3 Steel Tubes of minimum-wall-thickness, seamless and welded, carbon and alloy-steel tubes intended for use at low temperatures. For ASTM A334 Grade 3 Low-Temperature Tubes smaller than 1 ⁄ 2 in. [12.7 mm] in outside diameter
ASTM A334 Grade 3 Low-Temperature Seamless and Welded Tubes
ASTM A334 Grade 3 Low-Temperature Seamless and Welded Tubes
Standad:ASTM A334/A334M
Standard Specification for
Seamless and Welded Carbon and Alloy-Steel Tubes for Low-Temperature Service
ASTM A334 Grade 3 Steel Tubes of minimum-wall-thickness, seamless and welded, carbon and alloy-steel tubes intended for use at low temperatures. For ASTM A334 Grade 3 Low-Temperature Tubes smaller than 1 ⁄ 2 in. [12.7 mm] in outside diameter
ASTM A334 Grade 3 Low-Temperature Seamless and Welded Tubes Quick Details
Company Name: Beite steel pipe
Country/Region: China
Product Name：ASTM A334 Grade 3 Low-Temperature Tubes
Manufacture：seamless or automatic welding
Outside Diameter：3.4——12.7mm
Wall thickness：0.9mm——3mm
Length：6000mm、12000m or specified length as require
Port of Shipment：Tianjin,China
Payment：L/C or T/T
Delivery: 7-15 days after payment
Package: Bundles (hexagonal),Wooden Boxes,Crates (steel/wooden)
Materials and Manufacture
The tubes shall be made by the seamless or automatic welding process with no addition of filler metal in the welding operation.
Heat Treatment
Normalize by heating to a uniform temperature of not less than 1550 °F [845 °C] and cool in air or in the cooling chamber of an atmosphere controlled furnace.
For the seamless process only, reheat and control hot working and the temperature of the hot-finishing operation to a finishing temperature range from 1550 to 1750 °F [845 to 955°C] and cool in a controlled atmosphere furnace from an initial temperature of not less than 1550 °F [845 °C].
Chemical Composition of ASTM A334 Grade 3 Low-Temperature Tubes
| Element | Composition, % |
| Grade 3 | |
| Carbon, max | 0.19 |
| Manganese | 0.31–0.64 |
| Phosphorus, max | 0.025 |
| Sulfur, max | 0.025 |
| Silicon | 0.18–0.37 |
| Nickel | 3.18–3.82 |
| Chromium | ... |
| Copper | ... |
| Cobalt | ... |
| Molybdenum | ... |
Mechanical Properties of ASTM A334 Grade 3 Low-Temperature Tubes
| Grade 3 | ||
| ksi | MPa | |
| Tensile Strength, min | 65 | 450 |
| Yield Strength, min | 35 | 240 |
| Rockwell | B 90 | |
| Brinell | 190 | |
Mechanical property requirements do not apply to tubing smaller than 1 ⁄ 8 in. [3.2 mm] in outside diameter and with a wall thickness under 0.015 in.[0.4 mm].
Impact Temperature
| Grade | Impact Test Temperature | |
| °F | °C | |
| 3 | −150 | −100 |
Mechanical Tests
Tension Test
Flattening Test
Flare Test (Seamless Tubes)
Flange Test (Welded Tubes)
Reverse Flattening Test
Hardness Test
Impact Tests
Hydrostatic or Nondestructive Electric Test