ASTM A209 Grade T1 Seamless Boiler Tubes
- ASTM A209
- China
- Stock
- Grade T1
ASTM A209 Grade T1 Seamless BoilerTubes covers tubes 1 ⁄ 2 to 5 in. [12.7 to 127mm] inclusive, in outside diameter and 0.035 to 0.500 in. [0.9 to 12.7 mm], inclusive, in minimum wall thickness.
ASTM A209 Grade T1 Seamless Boiler Tubes
ASTM A209 Grade T1 Seamless Alloy-Steel Boiler and Superheater Tubes
Standard:ASTM A209/A209M
Standard Specification for
Seamless Carbon-Molybdenum Alloy-Steel Boiler and Superheater Tubes
ASTM A209 Grade T1 Steel Tubes covers several grades of minimum-wall-thickness, seamless, carbon-molybdenum alloy-steel,boiler and superheater tubes.
ASTM A209 Grade T1 Seamless BoilerTubes covers tubes 1 ⁄ 2 to 5 in. [12.7 to 127mm] inclusive, in outside diameter and 0.035 to 0.500 in. [0.9 to 12.7 mm], inclusive, in minimum wall thickness.
ASTM A209 Grade T1 Seamless Boiler Tubes Quick Details
Company Name: Beite steel pipe
Country/Region: China
Product Name：ASTM A209 Grade T1 Seamless Boiler Tubes
Manufacture：seamless process,hot-finished or cold-finished
Outside Diameter：12.7mm——127mm
Wall thickness：0.9mm——12.7mm
Length：6000mm、12000m or specified length as require
Port of Shipment：Tianjin,China
Payment：L/C or T/T
Delivery: 7-15 days after payment
Package: Bundles (hexagonal),Wooden Boxes,Crates (steel/wooden)
Materials and Manufacture
Steelmaking Practice—The steel shall be killed.
The tubes are made by the seamless process and shall be either hot-finished or cold-finished, as specified.
HeatTreatment
Hot-finished tubes shall be heat treated at a temperature of 1200 °F [650 °C] or higher.
Cold-finished tubes, after the final cold finishing, be heat treated at a temperature of 1200 °F [650 °C] or higher, or tubing may be furnished in the full-annealed, isothermal annealed, or normalized and tempered condition.
If furnished in the normalized and tempered condition, the minimum tempering temperature shall be 1200 °F [650 °C]
Chemical Composition
| Element | Composition, % |
| Grade T1 | |
| Carbon | 0.10–0.20 |
| Manganese | 0.30–0.80 |
| Phosphorus, max | 0.025 |
| Sulfur, max | 0.025 |
| Silicon | 0.10–0.50 |
| Molybdenum | 0.44–0.65 |
Mechanical Properties
| Mechanical Properties | Grade T1 |
| Tensile strength, min, ksi [MPa] | 55 [380] |
| Yield strength, min, ksi [MPa] | 30 [205] |
| Elongation in 2 in. or 50 mm, min, % | 30 |
| Brinell Hardness Number (Tubes 0.200 in. [5.1 mm] and over in Wall Thickness), HBW | 146 |
| Rockwell Hardness Number (Tubes less than 0.200 in. [5.1 mm] in Wall Thickness), HRB | 80 |
Forming Operations
Tubes when inserted in the boiler shall stand expanding and beading without showing cracks or flaws.
Tests
Flattening Test—One flattening test shall be made on specimens from each end ofone finished tube,
Flaring Test—One flaring test shall be made on specimens from each end ofone finished tube
Hardness Test—Brinell or Rockwell hardness tests shall be made on specimens from two tubes from each lot
Tension Test—One tension test shall be made on a specimen for lots of not more than 50 tubes. Tension tests shall be made on specimens from two tubes for lots of more than 50 tubes 