ASTM A312/A312M - 17 ——beite

Attention:     Issuing time:2018-02-28 09:45
ASTM A312 / A312M - 17 
 
Standard Specification for Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes
 
This guide covers standard specification for seamless, straight-seam welded, and cold worked welded austenitic stainless steel pipe intended for high-temperature and general corrosive service. Several grades of steel shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, chromium, nickel, molybdenum, titanium, columbium, tantalum, nitrogen, vanadium, copper, cerium, boron, aluminum, and others. All pipes shall be furnished in the heat-treated condition in accordance with the required heat treating temperature and cooling/testing requirements. Tensile properties of the material shall conform to the prescribed tensile strength and yield strength. The steel pipe shall undergo mechanical tests such as transverse or longitudinal tension test and flattening test. Grain size determination and weld decay tests shall be performed. Each pipe shall also be subjected to the nondestructive electric test or the hydrostatic test.
 
This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.
 

1. Scope
1.1 This specification2 covers seamless, straight-seam welded, and heavily cold worked welded austenitic stainless steel pipe intended for high-temperature and general corrosive service.

NOTE 1: When the impact test criterion for a low-temperature service would be 15 ft·lbf [20 J] energy absorption or 15 mils [0.38 mm] lateral expansion, some of the austenitic stainless steel grades covered by this specification are accepted by certain pressure vessel or piping codes without the necessity of making the actual test. For example, Grades TP304, TP304L, and TP347 are accepted by the ASME Pressure Vessel Code, Section VIII Division 1, and by the Chemical Plant and Refinery Piping Code, ANSI B31.3, for service at temperatures as low as −425 °F [−250 °C] without qualification by impact tests. Other AISI stainless steel grades are usually accepted for service temperatures as low as −325 °F [−200 °C] without impact testing. Impact testing may, under certain circumstances, be required. For example, materials with chromium or nickel content outside the AISI ranges, and for material with carbon content exceeding 0.10 %, are required to be impact tested under the rules of ASME Section VIII Division 1 when service temperatures are lower than −50 °F [−45 °C].

 
1.2 Grades TP304H, TP309H, TP309HCb, TP310H, TP310HCb, TP316H, TP321H, TP347H, and TP348H are modifications of Grades TP304, TP309Cb, TP309S, TP310Cb, TP310S, TP316, TP321, TP347, and TP348, and are intended for service at temperatures where creep and stress rupture properties are important.
 
1.3 Optional supplementary requirements are provided for pipe where a greater degree of testing is desired. These supplementary requirements call for additional tests to be made and, when desired, it is permitted to specify in the order one or more of these supplementary requirements.
 
1.4 Table X1.1 lists the standardized dimensions of welded and seamless stainless steel pipe as shown in ANSI B36.19. These dimensions are also applicable to heavily cold worked pipe. Pipe having other dimensions is permitted to be ordered and furnished provided such pipe complies with all other requirements of this specification.
 
1.5 Grades TP321 and TP321H have lower strength requirements for pipe manufactured by the seamless process in nominal wall thicknesses greater than 3/8 in. [9.5 mm].
 
1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.
 
NOTE 2: The dimensionless designator NPS (nominal pipe size) has been substituted in this standard for such traditional terms as “nominal diameter,” “size,” and “nominal size.”
 
 
2. Referenced Documents (purchase separately) 
 
ASTM Standards
A262 Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A941 Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys
A999/A999M Specification for General Requirements for Alloy and Stainless Steel Pipe
A1016/A1016M Specification for General Requirements for Ferritic Alloy Steel, Austenitic Alloy Steel, and Stainless Steel Tubes
E112 Test Methods for Determining Average Grain Size
E381 Method of Macroetch Testing Steel Bars, Billets, Blooms, and Forgings
E527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)
 
Other Standard
SAE J1086
 
ASME Standard
ASME Boiler and Pressure Vessel Code : Section VIII Available from American Society of Mechanical Engineers (ASME), ASME International Headquarters, Two Park Ave., New York, NY 10016-5990, http://www.asme.org.

ANSI Standards
B1.20.1 Pipe Threads, General Purpose
B36.10
B36.19 Stainless Steel Pipe


Main steel grades
TP304, TP304L, TP304H, TP321, TP316, TP316L, TP316H, TP347, TP347H
 
 
Chemical composition:
Steel Grade Chemical Composition%
C Mn P S Si Ci Ni Mo
TP304 0.08 2 0.045 0.03 0.75 18.0-20.0 8.0-11.0 /
TP304L 0.035 2 0.045 0.03 0.75 18.0-20.0 8.0-13.0 /
TP304H 0.04-0.10 2 0.045 0.03 0.75 18.0-20.0 8.0-11.0 /
TP316 0.08 2 0.045 0.03 0.75 16.0-18.0 11.0-14.0 /
TP316L 0.035 2 0.045 0.03 0.75 16.0-18.0 10.0-14.0 /
TP316H 0.04-0.10 2 0.045 0.03 0.75 16.0-18.0 11.0-14.0 /
TP321 0.08 2 0.045 0.03 0.75 17.0-19.0 9.0-12.0 /
TP347 0.08 2 0.04 0.03 0.75 17.0-20.0 9.0-13.0 /
TP347H 0.04-0.10 2 0.04 0.03 0.75 17.0-20.0 9.0-13.0 /
 
 
Mechanical behavior:
Steel Grade Mechanical behavior
Tensile Strength(MPa) Yield Strength(MPa) Elongation(%)
TP304 515 205 35
TP304L 485 170 35
TP304H 515 205 35
TP316 515 205 35
TP316L 485 170 35
TP316H 515 205 35
TP321 515 205 35
TP347 515 205 35
TP347H 515 205 35
 
 
Note:
HR:hot rolled CW:cold worked SR:stress relieved
A:annealed N:normalized HF



Contact:Lucky

whatapp: +8615003211561

E-mail:jinxiaolong0221@gmail.com
beitesteelpipe@gmail.com


 